Grüneberg, T: Improvement of selected properties of Wood-Pol

Wood Polymer Composites are a new group of hybrid materials, which combine the advantages
of synthetic polymers such as polyolefines and natural polymers such as wood; whereas the
synthetic polymer is used as matrix material and the wood as reinforcement material or filler. As
matrix material, principally every thermoplastic polymer with a processing temperature below
200°C can be used due to the temperature sensivity of wood. Wood Polymer Composites are
processed typically with processing technologies from the plastic industry such as extrusion and
injection molding.
The present study was conducted to explore the possibility of wood particle modification with
different types of silanes. It was the aim to contribute the silanes as compatibilizers or coupling
agent and therefore improve the mechanical properties and the resistance against water. Norway
spruce (Picea abies) as representative wood species was used in three different particle types. The
size distribution for the wood particles ranges from 70-2500 µm. Four commercial available
silanes with various functional groups (amino, di-amino, alkyl) were used as modification agents.
The concentrations varied between 1.5%, 3.0%, 4.5% and 7.5%. As reference system commonly
used maleated acid anhydride based coupling agents were used. The pre-treated wood particles
were compounded via extrusion with polypropylene and samples were produced via injection and
compression molding. The following properties were tested; tensile, bending, and impact
strength, water uptake (cold and boiling water test), descent rate, weathering tests and durability
test against basidiomycetes.
SEM-EDX investigations proved the presence of silane either in the cell wall structure, or on the
wood particle surface. Due to the structure and the functionality of the silanes it was expected
that the silane treated wood particles are able to improve the mechanical properties. It was shown
that the silanes had no significant